我所三明治结构加工论文（张文磊/刁东风）在国际期刊SCT上发表阅读次数 [1174] 发布时间 :2015-08-31 10:24:08
我所论文：Three-layered sandwich structured carbon film prepared by sputtering and ion/electron/ion alternative irradiation，发表于国际期刊Surface & Coatings Technology。
Three-layered sandwich structured carbon film prepared by sputtering and ion/electron/ion alternative irradiation Surface & Coatings Technology 278 (2015), 12-17(PDF-File) Wenlei Zhang, Dongfeng Diao*, Xue Fan The electron irradiated carbon film based on electron cyclotron resonance (ECR) sputtering technology has been proved to
have both high conductivity and paramagnetism. However, the relatively low hardness, wear life and high surface roughness value limit its application in Micro-electromechanical Systems (MEMS). To improve these properties, the sandwich structured carbon films with different modulation ratios were introduced on silicon (100) wafers by alternative irradiation (ion/electron/ion) technique in ECR sputtering system. The three-layered anostructure of films was measured with a transmission electron microscopy (TEM). The surface roughness of the film can be controlled to 0.19 nm according to the measurement of atomic force microscope (AFM). The unique characteristics of electron irradiated layer remained stable after irradiation through the analyzing of Raman spectroscopy. The mechanical properties (including hardness, elastic modulus, fracture behavior) and wear life were improved significantly due to the sandwich structure. The results showed that the sandwich structured carbon film is a kind of functional material equipped with enhanced mechanical and tribological properties.